C52100 Phosphor Bronze 8% C

Primary Designation:UNS C52100

Aliases:

Phosphor Bronze 8% Grade C8% Phosphor BronzeC52100

Mat Grades internal verification confirms source-backed fidelity and data integrity. It does not constitute external certification, ASTM/CDA endorsement, or guaranteed material conformity for procurement.

Compare Material Find Equivalents Open Family Hub

Data Completeness & Record Integrity:6 composition elements and 72 contextual property values cataloged.

Omitted fields represent unverified parameters. "Missing is better than invented."

Key Engineering Properties

Representative source rows, qualified by their reported conditions. Inspect the tables below for all values, limits, and source notes.

Density

8.802 g/cm³TYPICAL · at 20 °C

Electrical Conductivity

13 % IACSTYPICAL · at 20 °C

Thermal Conductivity

62.31 W/(m·K)TYPICAL · at 20 °C

Specific Heat Capacity

376.8 J/(kg·K)TYPICAL · at 20 °C

Melting Range (Solidus / Liquidus)

882.2 – 1026.7 °C1620.0 – 1880.0 °F

Solidus: 882.2°C | Liquidus: 1026.7°C

Composition Excerpt

Cu BALANCE wt%Copper (balance)

Standard Elemental Basis: BALANCE

Engineering Summary

UNS C52100 Phosphor Bronze (8% Sn, 0.03-0.35% P) offers significantly higher tensile strength and wear resistance than 5% phosphor bronze due to increased tin solid-solution hardening. Primarily specified for heavy-duty spring clips, clutch discs, musical instrument strings, and marine wear plates.

Documented Product Applications (Cited CDA Reference Profile)

›Architecture: Bridge Bearing Plates
›Beater Bar: Forming Characteristics
›Beater Bar: Friction & Wear Properties
›Beater Bar: Mechanical Properties
›Beater Bar: Thermal Properties
›Bellows: Corrosion Resistance
›Bellows: Forming Characteristics
›Bellows: Mechanical Properties
›Bourdon Tubing: Corrosion Resistance
›Bourdon Tubing: Forming Characteristics
›Bourdon Tubing: Mechanical Properties
›Bourdon Tubing: Thermal Properties

Recognized Aliases

Source-backed commercial trade name and short designations cataloged in canonical data.

Phosphor Bronze 8% Grade C8% Phosphor BronzeC52100

Standard Designations & Applicable Specifications

Semantically classified designations distinguishing primary standard identifiers, commercial trade names, and applicable specification references.

Direct Standard DesignationsDIRECT DESIGNATION

2 Primary Identifiers

System	Identifier	Standard System Name	Classification Notes & Provenance
UNSPRIMARY	C52100	Unified Numbering System	Unified Numbering System standard designation for copper alloys (CDA / SAE / ASTM)Ref: CDA UNS Standard Designations Register (C52100)
CDA	Alloy 521	Copper Development Association Alloy Number	CDA three-digit legacy designationRef: CDA UNS Standard Designations Register (C52100)

Recognized Commercial Aliases & Trade NamesCOMMON ALIAS

4 Listed

Recognized Name / Alias	Classification	Technical Usage & Context
Phosphor Bronze Grade C	Standard Commercial Name	CDA Standard Commercial Name
Phosphor Bronze 8% Grade C	Commercial Alias	Colloquial or commercial industry synonym
8% Phosphor Bronze	Commercial Alias	Colloquial or commercial industry synonym
C52100	Commercial Alias	Colloquial or commercial industry synonym

Applicable Specifications & Product Form ReferencesSPECIFICATION REFERENCE

9 Applicable Standards

Standards Body	Specification Code	Specification Title / Scope	Relationship Type
ASTM	ASTM B139/B139M	PHOSPHOR BRONZE ROD, BAR AND SHAPES	Specification Reference
ASTM	ASTM B103/B103M	PHOSPHOR BRONZE PLATE, SHEET, STRIP AND ROLLED BAR	Specification Reference
AWS	AWS A5.6	COPPER AND COPPER ALLOY COVERED ELECTRODES	Specification Reference
MILITARY	MILITARY MIL-E-23765/3	ELECTRODES, WELDING, BARE, COPPER AND COPPER ALLOY	Specification Reference
AWS	AWS A5.15	WELDING RODS FOR WELDING CAST IRON	Specification Reference
SAE	SAE J463	WROUGHT COPPER AND COPPER ALLOYS	Specification Reference
SAE	SAE J461	WROUGHT AND CAST COPPER ALLOYS	Specification Reference
ASTM	ASTM B888/B88M	COPPER ALLOY STRIP FOR USE IN MANUFACTURE OF ELECTRICAL CONNECTORS OR SPRING CONTACTS	Specification Reference
ASTM	ASTM B159/B159M	PHOSPHOR BRONZE WIRE	Specification Reference

Engineering Notice: Applicable specifications establish manufacturing requirements, dimensional tolerances, and test criteria for specific product forms (e.g. bus bar, wire, plate, pipe). They represent applicable technical standards, not alternative or equivalent alloy grades.

Chemical Composition (Weight %)

Elemental limits and values from the cited source. Preserves exact semantic limits (minimums, maximums, and ranges).

Element	Symbol	Atomic No.	Semantic Basis	Specified Value	Unit	Metallurgical Notes & Qualification	Data Status
Copper	Cu	29	BALANCE	Balance	wt%	Remainder element (Copper).Ref: Copper Development Association (CDA)	VERIFIED
Lead	Pb	82	MAXIMUM	≤ 0.05	wt%	CDA chemical composition specification limits for C52100: max 0.05 wt%.Ref: Copper Development Association (CDA)	VERIFIED
Tin	Sn	50	RANGE	7.00 – 9.00	wt%	CDA chemical composition specification limits for C52100: 7.0 - 9.0 wt%.Ref: Copper Development Association (CDA)	VERIFIED
Zinc	Zn	30	MAXIMUM	≤ 0.20	wt%	CDA chemical composition specification limits for C52100: max 0.2 wt%.Ref: Copper Development Association (CDA)	VERIFIED
Iron	Fe	26	MAXIMUM	≤ 0.10	wt%	CDA chemical composition specification limits for C52100: max 0.1 wt%.Ref: Copper Development Association (CDA)	VERIFIED
Phosphorus	P	15	RANGE	0.03 – 0.35	wt%	CDA chemical composition specification limits for C52100: 0.03 - 0.35 wt%.Ref: Copper Development Association (CDA)	VERIFIED

* Elemental percentages are expressed in weight percent (wt%). Values represent applicable specification limits. Unspecified trace elements are not fabricated or assumed.Preserves exact semantic basis

Property Display UnitsSwitch between Canonical SI and Source / US Customary units:

Physical Properties

Source-specific physical properties. Test temperatures are shown only where reported.

1 Parameters

Property Parameter	Canonical SI Value	Semantic Basis	Test Temperature / Context Range	Source Raw Reference	Source Reference	Status
Density	8.802 g/cm³	TYPICAL	Test Temp: 20 °CCDA Physical Properties: Density 0.318 lb/cu in. at 68°F (8.802 g/cm³ at 20°C)	0.318 lb/cu in. at 68°F	Copper Development Association Inc.	VERIFIED

Thermal & Thermodynamic Properties

Phase change temperatures, thermal conductivity, specific heat, mean coefficients of thermal expansion across standardized temperature ranges, and recommended thermal processing windows.

6 Parameters

Property Parameter	Canonical SI Value	Semantic Basis	Test Temperature / Context Range	Source Raw Reference	Source Reference	Status
Liquidus Temperature	1026.7 °C	TYPICAL	CDA Physical Properties: Liquidus temperature 1880.0 °F (1026.7 °C)	1880.0 °F	Copper Development Association Inc.	VERIFIED
Solidus Temperature	882.2 °C	TYPICAL	CDA Physical Properties: Solidus temperature 1620.0 °F (882.2 °C)	1620.0 °F	Copper Development Association Inc.	VERIFIED
Thermal Conductivity	62.31 W/(m·K)	TYPICAL	Test Temp: 20 °CCDA Physical Properties: Thermal conductivity 36.0 Btu/(ft·hr·°F) (62.31 W/(m·K) at 20°C)	36.0 Btu/ sq ft/ ft hr/ °F at 68°F	Copper Development Association Inc.	VERIFIED
Coefficient of Thermal Expansion (CTE)	18.18 µm/(m·K)	TYPICAL	CDA Physical Properties: CTE 10.1 µin/(in·°F) (18.18 µm/(m·K)) over range 68-57210°F	10.1 10^-6 per °F	Copper Development Association Inc.	VERIFIED
Specific Heat Capacity	376.8 J/(kg·K)	TYPICAL	Test Temp: 20 °CCDA Physical Properties: Specific heat 0.09 Btu/(lb·°F) (376.8 J/(kg·K))	0.09 Btu/ lb /°F at 68°F	Copper Development Association Inc.	VERIFIED
Annealing Temperature Range	482.2 – 676.7 °C	RANGE	CDA Thermal Treatments: Annealing temperature range 900 - 1250°F (482.2 - 676.7°C)	900 – 1250 °F	Copper Development Association Inc.	VERIFIED

Electrical Properties

Electrical conductivity and resistivity in their reported units and conditions.

1 Parameters

Property Parameter	Canonical SI Value	Semantic Basis	Test Temperature / Context Range	Source Raw Reference	Source Reference	Status
Electrical Conductivity	13 % IACS	TYPICAL	Test Temp: 20 °CCDA Physical Properties: Volume conductivity 13.0 % IACS at 68°F (20°C)	13.0 % IACS at 68°F	Copper Development Association Inc.	VERIFIED

Contextual Mechanical Properties & Tempers

Engineering strength, ductility, and hardness values grouped by product form, temper, and section thickness. Mechanical properties are contextual and not isotropic averages.

Elastic & Baseline Mechanical ConstantsSource-specific measurement conditions

Modulus of Elasticity (Tension)

110.3 GPa

CDA Physical Properties: Elastic modulus in tension 16000.0 ksi (110.3 GPa)

Modulus of Rigidity

41368.5 MPa

CDA Physical Properties: Shear modulus 6000.0 ksi (41368.5 MPa)

Machinability Rating

20 %

CDA Fabrication Properties: Rating relative to Free-Cutting Brass (C36000 = 100%).

Product Form:

Temper / Condition:

Showing 29 of 29 conditions

Product Form	Temper / Condition	Section Size	Tensile (UTS)	Yield Strength	Elongation	Shear Strength	Fatigue Strength	Hardness (Scales Preserved)	Status
Flat Products	1/2 Hard (H02) · 20 °C Source values and qualifiers Tensile Strength: 530.9 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Yield Strength (0.5% Ext): 441.3 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 in; Yield strength at 0.5% extension under loadCopper Development Association (CDA) — Elongation: 34 % (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — H02	0.04	530.9 MPa	441.3 MPa	34 %	—	—	—	VERIFIED
Flat Products	1/2 Hard (H02) Source values and qualifiers Rockwell B Hardness: 84 HRB (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Rockwell 30T Hardness: 73 HR30T (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — H02	0.04	—	—	—	—	—	84 HRB73 HR30T	VERIFIED
Flat Products	1/2 Hard and Stress Relieved (HR02) · 20 °C Source values and qualifiers Tensile Strength: 530.9 MPa (TYPICAL)Copper Development Association (CDA) — Yield Strength (0.5% Ext): 427.5 MPa (TYPICAL)Yield strength at 0.5% extension under loadCopper Development Association (CDA) — Elongation: 39 % (TYPICAL)Copper Development Association (CDA) — HR02	—	530.9 MPa	427.5 MPa	39 %	—	—	—	VERIFIED
Flat Products	Extra Hard (H06) · 20 °C Source values and qualifiers Tensile Strength: 723.9 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Yield Strength (0.5% Ext): 689.5 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 in; Yield strength at 0.5% extension under loadCopper Development Association (CDA) — Elongation: 9 % (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — H06	0.04	723.9 MPa	689.5 MPa	9 %	—	—	—	VERIFIED
Flat Products	Extra Hard (H06) Source values and qualifiers Rockwell B Hardness: 96 HRB (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Rockwell 30T Hardness: 80 HR30T (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — H06	0.04	—	—	—	—	—	96 HRB80 HR30T	VERIFIED
Flat Products	Extra Hard and Stress Relieved (HR06) · 20 °C Source values and qualifiers Tensile Strength: 723.9 MPa (TYPICAL)Copper Development Association (CDA) — Yield Strength (0.5% Ext): 641.2 MPa (TYPICAL)Yield strength at 0.5% extension under loadCopper Development Association (CDA) — Elongation: 15 % (TYPICAL)Copper Development Association (CDA) — HR06	—	723.9 MPa	641.2 MPa	15 %	—	—	—	VERIFIED
Flat Products	Extra Spring (H10) · 20 °C Source values and qualifiers Tensile Strength: 827.4 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Elongation: 2 % (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — H10	0.04	827.4 MPa	—	2 %	—	—	—	VERIFIED
Flat Products	Extra Spring (H10) Source values and qualifiers Rockwell B Hardness: 100 HRB (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Rockwell 30T Hardness: 82 HR30T (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — H10	0.04	—	—	—	—	—	100 HRB82 HR30T	VERIFIED
Flat Products	Hard (H04) · 20 °C Source values and qualifiers Tensile Strength: 641.2 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Yield Strength (0.5% Ext): 599.8 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 in; Yield strength at 0.5% extension under loadCopper Development Association (CDA) — Elongation: 19 % (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — H04	0.04	641.2 MPa	599.8 MPa	19 %	—	—	—	VERIFIED
Flat Products	Hard (H04) Source values and qualifiers Rockwell B Hardness: 93 HRB (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Rockwell 30T Hardness: 78 HR30T (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Fatigue Strength: 151.7 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 in; 10^8 cycles endurance limitCopper Development Association (CDA) — H04	0.04	—	—	—	—	151.7 MPa	93 HRB78 HR30T	VERIFIED
Flat Products	Hard and Stress Relieved (HR04) · 20 °C Source values and qualifiers Tensile Strength: 641.2 MPa (TYPICAL)Copper Development Association (CDA) — Yield Strength (0.5% Ext): 551.6 MPa (TYPICAL)Yield strength at 0.5% extension under loadCopper Development Association (CDA) — Elongation: 23 % (TYPICAL)Copper Development Association (CDA) — HR04	—	641.2 MPa	551.6 MPa	23 %	—	—	—	VERIFIED
Flat Products	Nominal Grain Size 0.015 mm (OS015) · 20 °C Source values and qualifiers Tensile Strength: 448.2 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Elongation: 60 % (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — OS015	0.04	448.2 MPa	—	60 %	—	—	—	VERIFIED
Flat Products	Nominal Grain Size 0.015 mm (OS015) Source values and qualifiers Rockwell F Hardness: 85 HRF (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — OS015	0.04	—	—	—	—	—	85 HRF	VERIFIED
Flat Products	Nominal Grain Size 0.025 mm (OS025) · 20 °C Source values and qualifiers Tensile Strength: 413.7 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Yield Strength (0.5% Ext): 165.5 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 in; Yield strength at 0.5% extension under loadCopper Development Association (CDA) — Elongation: 63 % (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — OS025	0.04	413.7 MPa	165.5 MPa	63 %	—	—	—	VERIFIED
Flat Products	Nominal Grain Size 0.025 mm (OS025) Source values and qualifiers Rockwell B Hardness: 50 HRB (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Rockwell F Hardness: 82 HRF (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — OS025	0.04	—	—	—	—	—	50 HRB82 HRF	VERIFIED
Flat Products	Nominal Grain Size 0.035 mm (OS035) · 20 °C Source values and qualifiers Tensile Strength: 399.9 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Elongation: 65 % (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — OS035	0.04	399.9 MPa	—	65 %	—	—	—	VERIFIED
Flat Products	Nominal Grain Size 0.035 mm (OS035) Source values and qualifiers Rockwell F Hardness: 80 HRF (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — OS035	0.04	—	—	—	—	—	80 HRF	VERIFIED
Flat Products	Nominal Grain Size 0.050 mm (OS050) · 20 °C Source values and qualifiers Tensile Strength: 379.2 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Elongation: 70 % (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — OS050	0.04	379.2 MPa	—	70 %	—	—	—	VERIFIED
Flat Products	Nominal Grain Size 0.050 mm (OS050) Source values and qualifiers Rockwell F Hardness: 75 HRF (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — OS050	0.04	—	—	—	—	—	75 HRF	VERIFIED
Flat Products	Spring (H08) · 20 °C Source values and qualifiers Tensile Strength: 772.2 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Yield Strength (0.5% Ext): 744.6 MPa (TYPICAL)Section Size: 0.04; Section Size: 0.04 in; Yield strength at 0.5% extension under loadCopper Development Association (CDA) — Elongation: 5 % (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — H08	0.04	772.2 MPa	744.6 MPa	5 %	—	—	—	VERIFIED
Flat Products	Spring (H08) Source values and qualifiers Rockwell B Hardness: 98 HRB (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — Rockwell 30T Hardness: 81 HR30T (TYPICAL)Section Size: 0.04; Section Size: 0.04 inCopper Development Association (CDA) — H08	0.04	—	—	—	—	—	98 HRB81 HR30T	VERIFIED
Flat Products	Spring and Stress Relieved (HR08) · 20 °C Source values and qualifiers Tensile Strength: 772.2 MPa (TYPICAL)Copper Development Association (CDA) — Yield Strength (0.5% Ext): 703.3 MPa (TYPICAL)Yield strength at 0.5% extension under loadCopper Development Association (CDA) — Elongation: 11 % (TYPICAL)Copper Development Association (CDA) — HR08	—	772.2 MPa	703.3 MPa	11 %	—	—	—	VERIFIED
Rod	1/2 Hard (H02) · 20 °C Source values and qualifiers Tensile Strength: 551.6 MPa (TYPICAL)Section Size: 0.5; Cold Work: 20%; Section Size: 0.5 inCopper Development Association (CDA) — Elongation: 33 % (TYPICAL)Section Size: 0.5; Cold Work: 20%; Section Size: 0.5 inCopper Development Association (CDA) — H02	0.5	551.6 MPa	—	33 %	—	—	—	VERIFIED
Rod	1/2 Hard (H02) Source values and qualifiers Rockwell B Hardness: 85 HRB (TYPICAL)Section Size: 0.5; Cold Work: 20%; Section Size: 0.5 inCopper Development Association (CDA) — H02	0.5	—	—	—	—	—	85 HRB	VERIFIED
Wire	1/2 Hard (H02) · 20 °C Source values and qualifiers Tensile Strength: 723.9 MPa (TYPICAL)Section Size: 0.08; Section Size: 0.08 inCopper Development Association (CDA) — H02	0.08	723.9 MPa	—	—	—	—	—	VERIFIED
Wire	1/4 Hard (H01) · 20 °C Source values and qualifiers Tensile Strength: 558.5 MPa (TYPICAL)Section Size: 0.08; Section Size: 0.08 inCopper Development Association (CDA) — H01	0.08	558.5 MPa	—	—	—	—	—	VERIFIED
Wire	Extra Hard (H06) · 20 °C Source values and qualifiers Tensile Strength: 965.3 MPa (TYPICAL)Section Size: 0.08; Section Size: 0.08 inCopper Development Association (CDA) — H06	0.08	965.3 MPa	—	—	—	—	—	VERIFIED
Wire	Hard (H04) · 20 °C Source values and qualifiers Tensile Strength: 896.3 MPa (TYPICAL)Section Size: 0.08; Section Size: 0.08 inCopper Development Association (CDA) — H04	0.08	896.3 MPa	—	—	—	—	—	VERIFIED
Wire	Nominal Grain Size 0.035 mm (OS035) · 20 °C Source values and qualifiers Tensile Strength: 413.7 MPa (TYPICAL)Section Size: 0.08; Section Size: 0.08 inCopper Development Association (CDA) — Yield Strength (0.5% Ext): 165.5 MPa (TYPICAL)Section Size: 0.08; Section Size: 0.08 in; Yield strength at 0.5% extension under loadCopper Development Association (CDA) — Elongation: 65 % (TYPICAL)Section Size: 0.08; Section Size: 0.08 inCopper Development Association (CDA) — OS035	0.08	413.7 MPa	165.5 MPa	65 %	—	—	—	VERIFIED

Hardness Integrity Notice: Rockwell B (HRB), Rockwell F (HRF), and Superficial 30T (HR30T) scales are reported on their measured scales without cross-scale mathematical conversion.

Source: See fact-level citations

Processing & Fabrication Characteristics

Machining, joining, forming, and thermal processing ratings cataloged from the cited authoritative technical reference.

Source: Copper Development Association (CDA)

Machinability

Machinability rating: 20% relative to free-cutting brass (C36000 = 100%).

Weldability & Joining

Soldering: Excellent; Brazing: Excellent; Oxyacetylene Welding: Fair; Gas Shielded Arc Welding: Good; Coated Metal Arc Welding: Fair; Spot Weld: Good; Seam Weld: Fair; Butt Weld: Excellent

Heat Treatment & Working Ranges

Annealing temperature range: 482.2°C to 676.7°C (900°F - 1250°F).

Forming & Cold Working

Capacity for Being Cold Worked: Good. Capacity for Being Hot Formed: Poor.

Comparable Grades & Cross-References

Carefully classified cross-reference relationships for C52100 Phosphor Bronze 8% C. Comparable does not mean equivalent.

Related Material	Family	Relationship Classification	Metallurgical Notes & Differences	Status	Action
C51000 Phosphor Bronze 5% A	Copper Alloys	Commonly Compared	C52100 contains 8% tin for higher mechanical strength and wear resistance in heavy-duty spring clips and clutch discs compared to 5% tin in C51000.Materials serve different design priorities (e.g. higher strength vs superior corrosion resistance or cost).	VERIFIED	Side-by-Side Compare →

Sources & Provenance Trail

Reference publications and standards organization registers cited across this material record.

Copper Development Association Inc.CDA Alloy C52100 Property & Specification Profile

AUTHORITATIVE BODY

Copper Development Association authoritative technical reference profile for C52100 Phosphor Bronze 8% C.

Issuing Body: Copper Development Association (CDA)View Source Record ↗

Copper Development Association Inc.CDA UNS Standard Designations Register (C52100)

AUTHORITATIVE BODY

Unified Numbering System (UNS) designation registration register confirming active C52100 status.

Issuing Body: Copper Development Association (CDA)View Source Record ↗